   Product Low Cement Castables

 

Sunward’s high strength low cement castables are made from superior refractory aggregate, ultra-fine powder, and special binder with low water content.
The advantages of Sunward’s low cement castable are:
1. High strength over a broad temperature range.
2. Excellent wear and corrosion resistance.
product photo
Specification

Brand

SNC-W45

SNC- W55

SNC- W60

SNC- W70

SNC- W80

SNC- W90

Properties

Bulk Density (g/cm3) 1500 (1450)℃ × 3 hrs

≧2.1

≧2.3

≧2.4

≧2.65

≧2.7

≧2.85

Cold Crushing Strength (kg/cm2)1500℃ × 3 hrs

≧600 

≧600 

≧550 

≧500 

≧600 

≧500 

Modulus of Rupture (kg/cm2) 1500℃× 3 hrs

≧100 

≧100 

≧80 

≧80 

≧120 

≧200 

Chemical Composition(%)

 

 

 

 

 

 

Al2O3

≧45

≧55

≧60

≧70

≧80

≧90

CaO

≦2

≦2

≦2

≦2

≦2

≦2.5

Cr2O3

---

---

---

---

---

---

SiC

---

---

---

---

---

---

Water Required (%)

7.5~8.5

6.5~7.5

6.5~7.5

6.0~7.0

5.5~6.5

5.0~5.5

Installation Method

Vibrating


Brand

SNC-S85

SNC- S60

SNC-M81

SNC- M82

Properties

Bulk Density (g/cm3) 1500 (1450)℃ × 3 hrs

≧2.4
(1450℃)

≧2.3
(1450℃)

≧2.4
(1450℃)

≧2.3
(1450℃)

Cold Crushing Strength (kg/cm2)1500℃ × 3 hrs

≧500
(1450℃)

≧500
(1450℃)

≧500
(1450℃)

≧500
(1450℃)

Modulus of Rupture(kg/cm2)
1500℃× 3 hrs

≧200
(1450℃)

≧180
(1450℃)

≧500
(1450℃)

≧70
(1450℃)

Chemical Composition(%)

 

 

 

 

Al2O3

---

---

≧65

≧55

CaO

---

---

---

---

Cr2O3

---

---

≧20

≧35

SiC

≧85

≧60

---

---

Water Required (%)

7.5~8.5

7.5~8.5

5.0~5.5

5.0~5.5

Installation Method

Vibrating

 